Copper 1% Silver-copper-phosphorus Brazing Alloy Welding Filler Metal

We are praised brand for Manufacturing, Exporting and Supplying 1% Silver-Copper-Phosphorus Brazing Alloy Welding Filler Metal from China, Nuevo Leon, Mexico.

Specifications

1. Low silver content.
2. Extremely fluid at brazing temperatures


HZ-Ag1P SILVER BRAZING ALLOY



COMPOSITION:

Silver 1.00 wt%

Phosphorus 6.00 wt%

Copper Balance

Tin 0.15 wt% max

Total Other Elements 0.15 wt% max.



MATERIAL PROPERTIES:

Solidus 1190oF (643A A C)

Liquidus 1510oF (821A A C)

Brazing Range 1450-1600oF (788-871A A C)

Specific Gravity 8.085

Density (toz/cu in) 4.261

Color Light Copper



DESCRIPTION:

HUAZHONG HZ-Ag1P is extremely fluid at brazing temperatures and will penetrate joint with very littleclearance. Melting of HZ-Ag1Pis virtually complete at 788A C.Best results areobtained when brazing slightly above Liquidus temperature with clearances of .001-.003". Thephosphorous content of HZ-Ag1Pacts as a fluxing agent and no flux is necessary whenbrazing copper to copper joints.However, when used with other compatible metals, a brazing flux must be used to promote wetting, bonding, and flow throughout the joint.



APPLICATIONS:
It is used for the brazing of copper and copper alloys, brass and bronze. It is primarily used for the joining of copper-to-copper on vibration free joints. It is very effective for joining tight fitting copper pipe and tubing. It should not be used on ferrous metalsor alloys containing more than 10% nickel due to the formation of brittle intermetallic phosphidecompounds.
AVAILABLE FORMS:
Standard forms of HZ-Ag1P are wire,flat wire, ring, strip, rod.