Epdm Water Proofing Sheets

In the view of our immense knowledge in this domain, we are counted amongst the most profound manufacturers and suppliers of EPDM Water Proofing Sheets. These sheets are used for water proofing purpose in vehicles and machine parts. The sheets are designed by our highly skilled workforce using optimum quality of rubber. Our quality inspectors check the EPDM Water Proofing Sheets on certain quality parameters before dealing with the clients. Features: Resistance against UV and high temperature Easy to install Flexible with high tensile strength  TECHNICAL SPECIFICATION - EPDM MEMBRANE BASED ON ASTM - D4637 EPDM MEMBRANE BASED ON ASTM - D4637 PROPERTIES TEST METHOD SPECIFICATION Tolerance on Nominal Thickness,% ASTM D 412 15/-10 Color Visual Black HARDNESS ASTM D2240 6510 Sh A TENSILE STRENGTH ( min ) ASTM D412 90KGS. CM2 ELONGATION AT BREAK ( min ) ASTM D412 350% TEAR RESISTANCE kg/cm ASTM D624 method C 30 Drop in physical properties - Ageing     After 100C for 600 Hrs     Tensile Strength min. ASTM D - 412 10% Elongation ( % ) ASTM D - 412 30% Tear resistance (kg/cm) ASTM - 412 15% Linear dimensional change max. % ASTM D - 1204 +/- 2% Ozone Resistance: On exposure to 100 ppm and Ozone in air 96 hrs.@ 40 C at 20 % strain ASTM D 1149 No crack Glass transition Temperature : ASTM D - 746 -55 Resistance Water absorption, after 7 days immersion in 70 C, % change in mass ASTM D 471 4.0 Compression set, 22 Hrs. at 70C ASTM D 395 24% Specification No: ZRWP100/1 Rev. No.: 00 Rev. Date: 00   TECHNICAL SPECIFICATION - EPDM MEMBRANE BASED ON ASTM 6134 EPDM MEMBRANE BASED ON ASTM 6134 PROPERTIES TEST METHOD SPECIFICATION Tolerance on Nominal Thickness,% ASTM D 412 15/-10 Color Visual Black HARDNESS ASTM D2240 65 10 A TENSILE STRENGTH ( min ) ASTM D412 90KGS.CM2 ELONGATION AT BREAK ( min ) ASTM D412 300% ABRASION RESISTANCE ( max ) ASTM D5963 250 mm3 COMPRESSION SET (70 C/24 hrs) (max) ASTM D395 Method B 24% TEAR RESISTANCE (Angular) min ASTM D624 method C 30 Resistance to Heat Aging     Properties after 166 hrs @ 115C  ASTM D - 573   Tensile Strength min. ASTM D - 412 85kgs. /Cm2 Elongation ( % ) ASTM D - 412 210 Linear dimensional change max. % ASTM D - 1204 +/-1 Brittleness temperature C ASTM D 746 -45 Resistance water absorption, after 166Hrs. Immersion @ 70 C     % change in mass ASTM D 471 4.0 Water Vapor Permeability Max. per-mills ASTM E 96 3.5 Specification No: RSWP100/2 Rev. No: 00 Rev. Date: 00   ZENA-SEAL TEST REPORT ZENA-SEAL TEST REPORT PROPERTIES TEST METHOD SPECIFICATION OBSERVATION Color Visual Black Black HARDNESS ASTM D2240 65 10 A 64,65,67 TENSILE STRENGTH ( min ) ASTM D412 90KGS. CM2 100,105,98 ELONGATION AT BREAK ( min ) ASTM D412 300% 400,450,400 ABRASION RESISTANCE ( max ) ASTM D5963 250 mm3 200 COMPRESSION SET ( 70 C / 24 hrs ) (max) ASTM D395 METHOD B 24% 20 TEAR RESISTANCE (Angular) min ASTM D624 method C 30 34,35,31 Resistance to Heat Aging       Properties after 166 hrs @ 115C ASTM D - 573     Tensile strength min. ASTM D - 412 85kgs. /Cm2 90,96,95 Elongation (%) ASTM D - 412 210 350,350,375 Linear dimensional change max. % ASTM D - 1204 +/-1 0.44 Brittleness temperature C ASTM D 746 -45 - Resistance water absorption, after 166Hrs. Immersion @ 70C       % change in mass ASTM D 471 4.0 3.45 Water Vapor Permeability Max. per-mils ASTM E 96 3.5 - Test report No: - ZSWP100/1 Rev. No:  00   Rev. Date: 00