Beryllium Copper Uns C17200 Alloy C17200 Din 2.1247 Wire

We are instrumental in exporting, distributing and supplying a broad variety of Beryllium Copper UNS C17200 Alloy C17200 DIN 2.1247 Wire in Mumbai, Maharashtra, India. Offered with us at rock bottom price range.

Product Details:-
Minimum Order Quantity50 Kilogram
Thickness0.04-5mm
Width10~200mm
GradeCopper Alloy

UNS C17200 beryllium copper alloys are ductile and produced in mill hardened and heat treatable tempers. These alloys are used for all applications, which require high strength, stiffness and good conductivity. The tensile strength of C17200 copper is over 1380 MPa (200 ksi).

The following datasheet will explain about UNS C17200 beryllium copper alloys.
Chemical Composition
The following table shows the chemical composition of UNS C17200 copper.
Element
Content (%)
Cu
97.9
Be
1.9
Co
0.20
Physical Properties
The physical properties of UNS C17200 copper are given in the following table.
Properties
Metric
Imperial
Density (during age hardening, 2% max. decrease in length and 6% max. increase in density)
8.25 g/cm3
0.298 lb/in3
Melting point
866C
1590F
Mechanical Properties
The mechanical properties of UNS C17200 copper are tabulated below.
Properties
Metric
Imperial
Hardness, Rockwell B
80.0 - 85.0
80.0 - 85.0
Tensile strength, ultimate
1280 - 1480 MPa
186000 - 215000 psi
Tensile strength, yield
965 - 1205 MPa
140000 - 174800 psi
Elongation at break
15.0 - 30.0%
15.0 - 30.0%
Modulus of elasticity
125 - 130 GPa
18100 - 18900 ksi
Poissons ratio
0.300
0.300
Machinability (UNS C36000 (free-cutting brass) = 100%)
20%
20%
Shear modulus
50.0 GPa
7250 ksi