Solar Eva Film By Shanghai Ever-thriving New Energy Technology Co., Ltd.

Our range of Solar EVA Film are available at following Features :-
(1) Low shrinkage, good encapsulation stability;
(2) Excellent transmittance, ensure high efficiency of PV components;
(3) Excellent aging resistance, low yellowish change;
(4) High gel content, ensure strength and dimension;
(5) Functional design, high adhesive strength with glass, solar cell, backsheets;
(6) Sufficient flexibility, less crack of solar cells during lamination
(7) Less bubble for solar cell encapsulation

Specification:
Adhesive strength with glass: a Y60 N/cm
Adhesive strength with BBF: a Y60 N/cm
Shrinkage Ratio on the glass (Machine direction): a 3.0%
Shrinkage Ratio on the glass (Crossing direction): a 2.0%
Shrinkage Ratio on the backsheet (Machine direction): a 3.0%
Shrinkage Ratio on the backsheet (Crossing direction): a 2.0%
Light Transmittance: a Y90.0%
Gel Content(150A C,30min): a Y80%
VA Content: 32%
Melting Point: 60 A C
Water-absorbing Ratio: <0.01%
UV Cut off Wavelength: 360 Nm
Volume Resistivity: 3.0A 1013 ICcm
Breakdown Voltage: 22.2KV/mm
Tensile Strength: 16.8Mpa
Elongation Ratio: 958.98%
Tensile modulus: 10.49Mpa
Thickness 0.30-0.80mm
Width 350-2000mm
Typical Range 810mm, 1000mm; 1100mm
Package 100m per roll